Mono Epoxy-Quart by Supermarine Paint
0 of 5 Stars
Mono Epoxy-Quart by Supermarine Paint
 
Size:
:
:
Quantity:
Price: $65.95
Sale Price: $59.98
 
 
Mono Epoxy (SM-2020) makes painting with epoxy marine paint easier than ever. It has quickly become a favorite of both the professional and the do-it-yourselfer because it eliminates the difficulty and hassle of mixing, induction time and the limited pot life that comes with catalyst cured two component epoxies. An advanced formula that produces an effective barrier to water and chemicals. It provides a high level of corrosion and chemical resistance while creating an effective barrier coat on a wide variety of surfaces in a marine environment.

Withstands long term submersion, heat (350F), corrosive chemicals, spilled fuel and staining agents. May be wet sanded and buffed. Acceptable for brush, roller-coat or spray applications. Brush: recommend natural bristle brushes. Roller: Recommend high quality dense foam roller covers. Spray: Recommend small-medium size tip. Dry to the touch in 1 hour, recoatable in 12 hours - temperature dependant. Dries hard in 24-48 hours. Sand between coats after 48 hours. Mixing ratio: N/A. Pot life: N/A. Covers 250-300 square feet per gallon. See label and application directions for further information. Available in 90 colors and in gloss or satin. Colors, excluding white and clear, are considered custom and therefore non-returnable.

Note: Darker Colors and Safety Colors containing SC in the part number are an additional $15 which is displayed after choosing that color. Safety Colors containing MT in the part number are an additional $20 which is displayed after choosing that color.

Shipping:  Ships within 2-4 days of order. 

  mono epoxy color chart



Product Details
Manufacturer: Supermarine Paint
Product SKU: SM-2020-Q
 


 

Product type: Epoxy Ester Copolymer Coating.

Product benefits: High Solid content, low V.O.C., hard yet flexible film, high gloss finish with good color retention, self priming on many surfaces, self leveling film, excellent adhesion to prepared surfaces, resistant to many alkalis, highly water-resistant, resistant to chalking, fading & chipping, resists peeling & cracking, weather-resistant, submersible long term.

Physical Characteristics:

Viscosity: 55-60 k.u. Dry to touch: 1-2 hours Weight solids: 34-36%

Recoat: 12-48 hours Volume solids: 29-31% WT per gal: 9.9 (White)

V.O.C.: 550 grams per liter Flash point: 105° F. Recommended WFT: 3-4 mils

Recommended DFT: 5 mils Coverage: 250-300 sq. ft. per gallon @ 3 mils wet

Recommendations: Recommend applying two or more coats to achieve a minimum DFT of 4 mils. Most applications will require dilution; See (SM-101 Thinner) do not substitute.

Cleaner: Recommend SM-695 Etching Cleaner for fiberglass, aluminum, concrete and prepared steel surfaces. Where rust is evident use SM-5679 Rust Converting Cleaner.

Primer:

Aluminum, galvanized and Stainless: Use SM-117 Pre-Wash Primer in combination with any other Supermarine primer.

Fiberglass use SM-664D Etching Primer or SM-7390 Formula 150 Epoxy Primer.

Steel, iron & concrete: SM-7390 Formula 150 Epoxy Primer or SM-787 Mono Epoxy Primer.

Wood: See SM-664D Etching Primer.

Slip Resistance: For added slip resistance add 8 ounces SM-630 Pro-Tex, 1 lb Tred-Tex or Gaco-Grip.

Clean up: Clean with Lacquer Thinner.

Accelerate/Harden: See SM-160 Accelerator/Hardener. Refer to Application Instructions Sheet, Product Data Sheet, label directions or contact us for additional information.

 

Applying Mono-Epoxy Marine Paint (SM-2020)

Mono Epoxy eliminates the difficulty of mixing multiple components together, induction time and limited pot life associated with traditional two-component marine epoxy. The single stage formula makes it easier to use and store for future use.

Unlike typical two-component marine epoxy Mono Epoxy produces a brushable self leveling finish making it remarkably easy to use. It utilizes the latest in modern marine coatings technology to achieve a longer lasting finish that is less likely to chalk and discolor. The cured finish is an effective barrier to both moisture and vapors on virtually any marine surface. It achieves a highly durable high-build protective finish that quickly self-levels to an exceptionally smooth yet rock hard finish.

Mono Epoxy produces a cured finish that retains its color and gloss better than typical two component epoxy reducing the likelihood of chalking and yellowing. It is easier to apply it lasts longer and saves you money on scheduled maintenance costs. It provides a high level of corrosion and chemical resistance while creating an effective barrier coat on a wide variety of surfaces in a marine environment. It is acceptable for use on most any marine surface. Value, durability and ease of application makes Mono Epoxy a compelling choice.

PRODUCT SPECIFICATIONS

Product type: Epoxy Ester Copolymer Coating.

Product benefits: High Solid content, low V.O.C., hard yet flexible film, high gloss finish with good color retention, self priming on many surfaces, self leveling film, excellent adhesion to prepared surfaces, resistant to many alkalis, highly water-resistant, resistant to chalking, fading & chipping, resists peeling & cracking, weather-resistant, submersible long term.

Physical Characteristics:

Viscosity: 55-60 k.u. Dry to touch: 1-2 hours Weight solids: 34-36%

Recoat: 12-48 hours Volume solids: 29-31% WT per gal: 9.9 (White)

V.O.C.: 550 grams per liter Flash point: 105° F. Recommended WFT: 3-4 mils

Recommended DFT: 5 mils Coverage: 250-300 sq. ft. per gallon @ 3 mils wet

SUNDRIES

Sandpaper-80 grit for repairs 120 grit for rough sanding-180 grit for finish sanding. Mohair or wool roller covers, roller frame, roller tray and natural bristle brushes. Rubber gloves, canister type air filter for spray applications.

RECOMMENDED CLEANERS

SM-695 Etching Cleaner de-waxes, cleans and deglazes most any surface. Where rust is present recommend SM-5679 Rust Converting Cleaner.

RECOMMENDED PRIMERS

Aluminum: SM-117 Pre-Wash Primer, SM-664D Etching Primer or SM-7390 Formula 150 Polyamide Epoxy Primer.

Fiberglass: SM-664D Etching Primer or SM-7390 Formula 150 Epoxy Primer.

Wood: SM-664D Etching Primer.

Steel: SM-787 Mono Epoxy Primer, SM-1184 Zinc Chromate Primer, SM-1757 Zinc-Plate Primer, SM-5000 Zinc Plate, SM-7390 Formula 150 Polyamide Epoxy Primer.

RECOMMENDED THINNER

SM-101 Thinner. Do not substitute.

ACCELERATOR/HARDENER

SM-160 Accelerator/Hardener accelerates, hardens improves corrosion and chemical resistance. (recommended for hull, decks, engine room, and high abuse/traffic areas).

APPLICATION

All applications should begin with the removal of hardware, ventilators, bang irons and decorative name plates. After that, the steps to prepare a boat for paint or a clear coating are only slightly different from those taken with wood, fiberglass, aluminum or steel. The difference between an amateur and professional application is often preparation. The smart painter puts most of his effort into preparing the boat for painting. The old saying is true that 99 % of a good paint job lies in preparation and 99% of paint failures are due to poor preparation. This is a statistic you do not want applied to your project! Do not cut corners when preparing your boat for paint!

Previously painted boats: Best results will be achieved when most or all old paints have been completely *removed and primer applied to all surfaces, however, paint in good condition may be cleaned and de-waxed with SM-695 Etching Cleaner then sanded with 100 grit sandpaper in preparation for paint. An orbital palm sander or dual-action rotary sander will be less strenuous than hand sanding. Sanding will reveal areas that are blistered or flaking requiring removal. Such areas should be repaired if needed and properly primed. Hand sand to feather the repair to the level of the rest of the existing paint for best results. Scrapes, scratches and divots may be filled with painter's glazing compound prior to painting. Trowel it into the blemish with a putty knife allowing it to set up before sanding smooth. All repairs and glazing compounds should be primed and sanded before proceeding with paint.

Preparation on Fiberglass & Aluminum: Loose scale, peeling or cracking paint, corrosion, dirt, grime, oil, grease and wax all must be thoroughly *removed. Always clean thoroughly before making any repairs or sanding. Wax removal is critical and should be done with SM-695 Etching Cleaner or a commercial wax remover. Where silicone polishes are present be sure to use a blended solvent polish remover to remove silicone. A second application of cleaner is helpful. Once cleaned, gouges and scrapes may be filled with epoxy putty. Build up the epoxy above the surrounding surface so that it can be sanded smooth. Epoxy filler is hard so power sanding is advised. A dual-action rotary sander achieves the best results however a good orbital palm sander is acceptable. Rough sand the patch with 80 grit then switch to 120 grit sandpaper to achieve the final contour. Once repairs have been completed sand the entire area to be refinished with 120 to 180 grit sandpaper then clean with a pre-paint cleaner or recommended solvent.

Preparing Raw Wood (Unpainted): Bare wood should be sanded smooth with 80 grit paper before the application of SM-664D Etching Primer. Select this primer to fill the grain of the wood and create a smooth easy to adhere to surface for the paint. It has an unusually high amount of solid material, sands beautifully and locks our air and moisture. Recommend allowing primer to dry for 2-4 hours before sanding with 120 grit paper. Often repeated coats are applied to achieve a smooth finished surface. Repeated primer coats and sanding may be continued until the grain has been filled and the surface is completely smooth. Recommend 180 grit sandpaper for use in finish sanding.

Fasteners in wood hulls are always countersunk below the surface of the planks. It is necessary to fill these countersinks in order to achieve a completely smooth finish. Surfacing putties are preferred over epoxy or polyester putties because epoxy putties can be harder to remove should it ever become necessary to remove a plank for repair.

Carvel planked boats require a seam compound. Traditional seam compounds are never applied until after the hull has received a primer base coat. Traditional seam compounds should never be applied to bare wood, however, polysulfide seam compounds must be applied only to bare wood. Apply polysulfide seam compounds into the seam prior to applying primer.

Preparing Wood (Previously Painted): Paint in good condition should be sanded with 120 grit paper to knock off the gloss. Orbital palm sanders or dual action rotary sanders make *sanding large areas much easier. Sanding usually reveals paint that has blistered or flaked requiring scraping the hull and sanding to bare wood. Such areas should filled, primed and sanded smooth.

The inevitable sunken fastener holes, scratches and dings should be filled with painter's glazing compound - not to be confused with glazing putty used to keep glass in home windows. Marine glazing compound is a fine putty intended for repairing small surface blemishes prior to painting. Apply to the blemish area with a putty knife, allow it to cure thoroughly then sand surface to a smooth finish.

Deteriorating Paint should be completely removed from the hull before repairs or primer is applied. Power sanding is preferred over paint remover. This process is referred to as "wooding down." Once the old paint has been removed prepare the hull as if it were new bare wood.

Preparation on Steel: Proper surface *preparation is vital. Previously painted surfaces must be thoroughly cleaned and free of residues, oily film, and loose paint chips. All rust, loose scale and contaminates must be thoroughly *removed prior to the application of primer. Preparation should include wire brushing by hand, mechanical grinding and or sand blasting of all surfaces. Rust should be treated with SM-5679 Phos-Pro Rust Converting Metal Conditioner. Rust free and galvanized metals should be treated with SM-695 Etching Cleaner. Once all surfaces have been carefully prepared, rust, oil, grease and contaminates removed, the application of recommended primer should be applied without delay to prevent new corrosion. Surfaces treated with SM-5679 Rust Converting Cleaner must be primed within 24 hours (See Performance Data Sheets and MSDS for SM-5679 Rust Converting Cleaner and SM-695 Etching Cleaner for further information).

Primer: Aluminum, fiberglass, existing epoxy and gel coat are "hard to paint" surfaces requiring an etching primer. SM-664D Etching Primer is recommended for use on all gel coat, epoxy, raw fiberglass and wooden surfaces. It is a superior government specification formula (TT-P-664D) that is very well liked in this application. While epoxy primer will work SM-664D Etching Primer outperforms epoxy primers on hard to paint surfaces. You will find Etching Primer provides outstanding adhesion, build, sandability and protection from corrosion on almost any marine substrate. Its use results in better adhesion of the finish coat than can be obtained by any other process. It may applied with a brush, roller or sprayed. Using a roller speeds up the work and provides a higher film thickness than spraying. Apply a minimum of one evenly applied coat to all areas that will be painted. Film build is high making sanding surprisingly easy. Use Etching Primer as filler by simply building it up with a brush, allowing it to dry then sanding it smooth. When spraying Etching Primer it will likely need to be thinned with SM-605 Thinner. Do not substitute with other thinners. Galvanized steel, stainless steel and anodized surfaces must be treated with a fog coat of SM-117 Prewash Primer. We recommend using SM-664D, SM-787, SM-5000 or SM-7390 Primer as an intermediate primer coat before the application of Revolution.

Finish Coats: Fiberglass, Aluminum & Steel: Professionally applied spray coat applications yield superior results, however Mono Epoxy levels exceptionally well in brush and roll applications. Unless you are experienced with spray equipment the best way for the do it yourselfer is to apply Mono Epoxy is by roller coat. When properly thinned in appropriate temperatures (SM-101 Thinner 5%-10%) Mono Epoxy levels well. It had a good defoamer "bubble popping additive" reducing the importance of tipping. Aside from spraying, which offers the best film thickness control, rolling is often the best way to achieve the recommended wet film thickness, 3-4 mils WFT (Wet Film Thickness). The recommended DFT is 5 mils. Applications applied too thickly may not adhere or level properly, run, sag and take days, or even longer to cure. Always adhere to the manufacturers recommended WFT and DFT (Dry Film Thickness)!

Mono Epoxy must always be stirred or shaken thoroughly before use. It may be brushed, rolled or sprayed utilizing conventional and HVLP spray equipment. Thinning will be necessary is most applications. The amount of thinner (SM-101Thinner) required will vary depending on ambient temperature, type of equipment used, method of application, humidity, color and amount of control desired and tip size in spray applications. We suggest beginning by thinning 5% at first with 5-10% with SM-101 Thinner and increasing dilution as needed subject to your individual application requirements.

Mono Epoxy may be built up to achieve a higher DFT where desired. Two, three or more coats are acceptable to achieve the recommended DFT. Boot and bottom stripes should always be applied over top of the recommended DFT. For best results recoat within 24-48 hours or sand between applications. Allow top coat film to cure thoroughly before allowing it to enter full service duty. The recommended minimum cure time is 5-7 days under most conditions. DO NOT allow newly applied paint to get wet for a minimum of 48 hours. The dry cured film may be wet sanded and buffed to remove runs and blemishes.

What should I watch out for?

INCOMPATABILITY ISSUES: Mono Epoxy belongs to a classification of coatings referred to as "long-oils". While long oils may be applied over virtually any surface or existing coating they may NOT be over coated with products that include high percentages of lacquer, xylene, toluol or similar "hot" solvents. Our guaranty is void unless applied at the recommended thickness and used only with recommended Supermarine cleaners, thinners, accelerator/hardener and primers. When painting over preexisting primer or paint be sure it has cured before proceeding.

SOFTNESS OR WRINKLING: Strictly adhere to manufacturers recommended minimum and maximum WFT and DFT. When Mono Epoxy has been applied too thickly the coating may not catalyze properly which may lead to extended dry and cure times or prolonged softness of the film. Runs and sags: If you get runs or sagging it has likely been applied to thick. This product may be different than what you may have used previously. Recommend doing a small test before committing to the entire project. Testing the product will give you a feel for the product resulting in fewer problems.

DRYING PROBLEMS /SLOW CURING: Mono Epoxy is catalyzed by oxygen rather than chemically. The full cure may take longer to achieve than expected. The curing process should be allowed to be completed naturally or with the addition of SM-160 Accelerator/Hardener before entering full service duty or film failure may occur. When you cannot mark it with your fingernail you know it has cured enough to enter full duty service. When the film remains soft after 48 hours it has likely been applied too heavily. Dark and MT colors are typically slower to dry and cure. Using SM-160 A/H forced drying (adding heat such as oven baking) or increasing air movement across the curing film are ways to speed dry and cure times. Allow more time (weeks if needed) until the film has cured. If after several weeks the film is still soft it will likely require removal and replacement. The use of SM-160 A/H is optional. It's use increase hardness, chemical resistance and speeds cure times.

 
 
We Also Recommend:

Supermarine Leveling Thinner-SM101
Supermarine Leveling Thinner-SM101 Leveling Thinner (SM-101) is a proprietary blend of solvents that include effective conditioning and drying agents. For best results use only where re...
view more!
Accelerator/Hardener for Supermarine Paint
Accelerator/Hardener for Supermarine Paint Accelerator/Hardener (SM-160) An optional accelerator/hardener for use with SM-1000 Revolution and SM-2020 Mono Epoxy color coatings and clears. When ...
view more!
Supermarine Pre-Treatment Wash Primer
Supermarine Pre-Treatment Wash Primer Supermarine Pre-Treatment Wash Primer (SM-117) is a Chromate Polyvinyl Butyral Two-Component Etching Wash Primer used on hard to adhere to aluminum, g...
view more!
Pro-Tex Texture Additive for Supermarine Paint
Pro-Tex Texture Additive for Supermarine Paint Pro-Tex Texture Additive is a micronized wax additive for liquid coatings that creates a textured slip resistant finish to any paint or clear coating ...
view more!
Quick-Dry Synthetic Thinner for Supermarine Paint
Quick-Dry Synthetic Thinner for Supermarine Paint Quick-Dry Synthetic Thinner (SM-605) A proprietary formula that speeds the flash time. Use where recommended for best results. It thins, conditions an...
view more!
Mono Epoxy Primer-SM-787
Mono Epoxy Primer-SM-787 Shipping:Ships within 2-4 days of order.Supermarine Mono-Coat Epoxy Primer (SM-787) is a one of a kind single component oxygen cured epoxy primer that...
view more!
Supermarine Etching Primer
Supermarine Etching Primer Supermarine Etching Primer (SM-664D) is our best selling and most popular marine primer because of its versatility, outstanding sandability and protec...
view more!
Etching Cleaner Concentrate-SM695
Etching Cleaner Concentrate-SM695 Etching Cleaner Concentrate (SM-695) Excellent for use as a pre-paint cleaner. Cleans and removes rust, corrosion, oxidation, wax, grease, oil and sim...
view more!
 
Customers who bought this product also purchased...

White Gelcoat by Sea Hawk Paints
White Gelcoat by Sea Hawk Paints
Always Free Shipping
Premium Marine Grade White Gel Coat has great cosmetic and protective life expectancy and will keep your hull shining like new for years. Sea Hawk whi...
view more!
Hawk Filler-Epoxy Filler .5 Gallon Kit
Hawk Filler-Epoxy Filler .5 Gallon Kit
Always Free Shipping
Hawk Filler and be used above or below the waterline for repairingblisters, cracks, joints and scratches in gelcoat and fiberglass. Sea Hawk's Haw...
view more!
Economy Roller Frame 4"
Economy Roller Frame 4 4-Wire Cage 1/4" Shank Threaded Plastic Grip. For a 4 inch roller cover.
view more!
Wax N Grease Killer Solvent Wash
Wax N Grease Killer Solvent Wash Every new fiberglass hull produced is released from the mold by a mold release wax. In order to obtain proper adhesion of paint, the wax and other for...
view more!
Europa 2.5 inch Soft Badger Style China Bristle Brush
Europa 2.5 inch Soft Badger Style China Bristle Brush Europa Soft badger-style pure China bristle. Extra fine tip. Hand formed chisel. Black lacquered hardwood special peg handle. Stainless steel ferrule....
view more!
Roller Cover Red Mohair 3/16 Nap 7"
Roller Cover Red Mohair 3/16 Nap 7 Synthetic Paint Roller Cover - 2-Ply Polypropylene Cores - Professional Quality, for All Paints
view more!
 
 
 
 
Copyright © 2014 BottomPaintStore.com. All rights reserved.
About Us   |   Contact Us   |   Wholesale Account   |   Shipping   |   Industry Links   |   No Sales Tax   |  Terms and Conditions   |   Shopping Cart   |   Site Map